5CrNiMo

2019-10-31
5CrNiMo
詳細介紹:

5CrNiMo鋼具有良好的韌性、強度和高耐磨性,屬熱作模具鋼。它在室溫和500~600℃時的力學性能幾乎相同。在加熱到500℃時,仍能保持住HB300左右的硬度。由于鋼中含有鉬,因而對回火脆性并不敏感。從600℃緩慢冷卻下來以后,沖擊韌性僅稍有降低。


化學成份


碳 C :0.50~0.60

硅 Si:≤0.40

錳 Mn:0.50~0.80

硫 S :≤0.030

磷 P :≤0.030

鉻 Cr:0.50~0.80

鎳 Ni:1.40-1.80

銅 Cu:允許殘余含量≤0.30

鉬 Mo:0.15~0.30


硬度:退火,241~197HB,壓痕直徑3.9~4.3mm


技術參數


淬火后 :58

淬火溫度℃ :830~860

交貨狀態 :退火HB≤241

冷卻劑 :油Oil


自由鍛件公司哪家好,就找唐山盛通鍛造有限公司。


5CrNiMo steel has good toughness, strength and high wear resistance, and is a hot work die steel. It has almost the same mechanical properties at room temperature and 500 to 600 °C. When heated to 500 ° C, it can still maintain the hardness of HB300. Because steel contains molybdenum, it is not sensitive to temper brittleness. After slowly cooling from 600 ° C, the impact toughness was only slightly reduced.


chemical composition


Carbon C: 0.50~0.60

Silicon Si: ≤ 0.40

Mn: 0.50 to 0.80

Sulfur S :≤0.030

Phosphorus P :≤0.030

Chromium Cr: 0.50~0.80

Nickel Ni: 1.40-1.80

Copper Cu: Allowable residual content ≤ 0.30

Molybdenum Mo: 0.15~0.30


Hardness: Annealed, 241 ~ 197HB, indentation diameter 3.9 ~ 4.3mm


technical parameter


After quenching: 58

Quenching temperature °C: 830 ~ 860

Delivery status: Annealing HB≤241

Coolant : Oil Oil